Ṣiṣeto iṣẹ lilọ ti awọn kẹkẹ lilọ nipasẹ granularity adalu ti abrasives

Lilọ jẹ ilana ṣiṣe ẹrọ eyiti kẹkẹ lilọ abrasive (GS, bi a ti fun ni Fig.1) jẹ lilo lati yọ awọn ohun elo kuro ni iyara yiyi kan [1]. Awọn kẹkẹ lilọ jẹ ti awọn abrasives, oluranlowo abuda, awọn kikun ati awọn pores, bbl Ninu eyiti, abrasive ṣe ipa ti gige gige lakoko ilana lilọ. Agbara, agbara, awọn ihuwasi fractural, geometry ti abrasive ni ipa pataki lori iṣẹ lilọ (agbara lilọ, iduroṣinṣin dada ti iṣẹ iṣẹ ẹrọ, ati bẹbẹ lọ) ti kẹkẹ lilọ [2, 3].

aworan 1.Awọn aṣoju lilọ wili pẹlu adalu granularity ti abrasives.

Agbara zirconia alumina (ZA) pẹlu granularity ti F14 ~ F30 ni idanwo. Awọn akoonu abrasive ti F16 tabi F30 ni GS ti a pese silẹ ni a pin si awọn onipò marun lati giga si kekere: ultrahigh (UH), giga (H), arin (M), kekere (L), ati iwọn kekere (EL). A rii pe agbara fifọ Weibull ti F14, F16 ati F30 ti ZA jẹ 198.5 MPa, 308.0 MPa ati 410.6 MPa, ni atele, ti o fihan pe agbara ti ZA dagba pẹlu idinku ti iwọn grit abrasive. Awọn tobi Weibull modulusmtọkasi iyatọ ti o kere si laarin awọn patikulu idanwo [4-6]. Awọnmiye dinku pẹlu idinku ti abrasives grit iwọn, fifihan pe iyatọ laarin awọn abrasives idanwo ti di nla pẹlu idinku ti grit abrasive [7, 8]. Niwọn igba ti iwuwo abawọn ti abrasive jẹ igbagbogbo, awọn abrasives ti o kere ju ni awọn iwọn kekere ti awọn abawọn ati agbara ti o ga julọ, nitorinaa jẹ ki awọn abrasives ti o dara julọ nira lati fọ.

Eeya.2. Wahala abuda Weibulls₀ati modulus Weibullmfun orisirisi granularities ti ZA.

Awoṣe yiya okeerẹ abrasive ti ilana iṣẹ ṣiṣe pipe ni idagbasoke [9], bi a ti ṣe apejuwe rẹ ni aworan 3. Labẹ awọn ipo ti o dara julọ, abrasive ni iwọn lilo giga ati GS ṣe afihan iṣẹ lilọ to dara [3]. Labẹ fifuye lilọ ti a fun ati agbara oluranlowo abuda, awọn ọna ẹrọ yiya akọkọ ni a yipada lati yiya attrition ati micro-facture fun F16 si yiya attrition ati fa-jade fun nini F30 si iyatọ ninu agbara fifun abrasive [10,11]. Yiya atrition ti fa ibajẹ GS ati didan ara ẹni ti o fa nipasẹ abrasive fa-jade le ṣaṣeyọri ipo iwọntunwọnsi, nitorinaa igbega agbara lilọ ni pataki [9]. Fun idagbasoke siwaju sii ti GS, agbara fifun abrasive, agbara oluranlowo abuda ati fifuye lilọ, bakanna bi awọn ilana wiwọ ti awọn iyipada ti abrasives, yẹ ki o ṣatunṣe ati iṣakoso lati ṣe igbelaruge oṣuwọn lilo abrasives.

Eeya.3.Awọn bojumu iṣẹ ilana ti ẹya abrasive

Botilẹjẹpe iṣẹ lilọ ti GS ni ipa nipasẹ ọpọlọpọ awọn ifosiwewe, gẹgẹ bi agbara fifun abrasive, agbara oluranlowo abuda, fifuye lilọ, awọn ihuwasi gige abrasive, awọn ipo lilọ, ati bẹbẹ lọ, awọn iwadii ti awọn ilana ilana ti awọn granularities adalu ti abrasives le pese itọkasi nla lori apẹrẹ ati iṣelọpọ ti GS.

Awọn itọkasi 

• I.Marinescu, M. Hitchiner, E. Uhlmanner, Rowe, I. Inasaki, Handbook ti machining pẹlu lilọ kẹkẹ, Boca Raton: Taylor & Francis Group Crc Press (2007) 6-193.
• F. Yao, T. Wang, JX Ren, W. Xiao, Iwadi afiwera ti aapọn iyokù ati ipele ti o kan ni Aermet100 irin lilọ pẹlu alumina ati awọn kẹkẹ cBN, Int J Adv Manuf Tech 74 (2014) 125-37.
• Li, T. Jin, H. Xiao, ZQ Chen, MN Qu, HF Dai, SY Chen, Topographical characterization ati yiya ihuwasi ti kẹkẹ diamond ni orisirisi awọn ipele processing ni lilọ ti N-BK7 opitika gilasi, Tribol Int 151 (2020) 106453.
• Zhao, GD Xiao, WF Ding, XY Li, HX Huan, Y. Wang, Ipa ti awọn akoonu ọkà ti oka kan ti o ni idapọ cubic boron nitride lori ilana yiyọ ohun elo nigba Ti-6Al-4V alloy lilọ, Ceram Int 46 (11) (2020) 17666-74.
• F. Ding, JH Xu, ZZ Chen, Q. Miao, CY Yang, Awọn abuda wiwo ati ihuwasi fracture ti brazed polycrystalline CBN oka lilo Cu-Sn-Ti alloy,Mat Sci Eng A-Struct 559 (2013) 629-34.
• Shi, LY Chen, HS Xin, TB Yu, ZL Sun, Iwadi lori awọn ohun-ini lilọ ti imudara igbona giga vitrified CBN lilọ kẹkẹ fun titanium alloy, Mat Sci Eng A-Struct 107 (2020) 1-12.
• Nakata, AFL Hyde, M. Hyodo, H. Murata, A iṣeeṣe ona to iyanrin patiku crushing ni triaxial igbeyewo, Geotechnique49 (5) (1999) 567-83.
• Nakata, Y. Kato, M. Hyodo, AFL Hyde, H. Murata, Ọkan-onisẹpo iwa funmorawon ti uniformlygrade iyanrin jẹmọ si nikan patiku crushing agbara, Ile ri 41 (2) (2001) 39-51.
• L. Zhang, CB Liu, JF Peng, ati be be lo. Imudarasi iṣẹ lilọ ti iṣinipopada iyara-giga ti o lọ okuta nipasẹ granularity adalu ti zirconia corundum. Tribol Int, 2022, 175: 107873.
• L. Zhang, PF Zhang, J. Zhang, XQ Fan, MH Zhu, Ṣiṣayẹwo ipa ti iwọn grit abrasive lori awọn ihuwasi lilọ iṣinipopada, J Manuf Process53 (2020) 388-95.
• L. Zhang, CB Liu, YJ Yuan, PF Zhang, XQ Fan, Ṣiṣayẹwo ipa ti yiya abrasive lori iṣẹ lilọ ti awọn okuta lilọ iṣinipopada, Ilana J Manuf 64 (2021) 493-507.